A537Cl 1+304 L CLAD asye plak konpozisyon chimik ak pwopriyete mekanik
|
A537 Klas 3Konpozisyon chimik |
|||||||||
|
Egalize |
Eleman max la (%) |
||||||||
|
C |
Mn |
P |
S |
Si |
CU |
NI |
Cr |
Mwa |
|
|
A537 Klas 3 |
0.24 |
0.92-1.72 |
0.035 |
0.035 |
0.13-0.55 |
0.38 |
0.28 |
0.29 |
0.09 |
|
Egalize |
A537 Klas 3 pwopriyete mekanik |
|||
|
Epesè |
Rekòlt |
Raman |
Elongasyon |
|
|
A537 Klas 3 |
mm |
Min MPA |
MPA |
Min % |
|
-65 |
380 |
550-690 |
22 |
|
|
65-100 |
345 |
515-655 |
20 |
|
|
100-150 |
275 |
485-620 |
- |
|
| Egalize |
C
|
Mn |
P
|
S
|
Si |
Cr |
NI | Mwa | NI |
Koper
|
| 304L(S30403) | 0.030 | 2.0 | 0.045 | 0.030 | 0.75 | 17.5-19.5 | 8.0-12.0 | - | 0.10 | - |
| Egalize |
Sede fòs (N/mm2), min |
Fòs rupture (N/mm2), min |
Elongationin 2 pous (50mm), %, min |
|
Fwad Bend | ||||||
|
Austenitic (CHROMIUM - NICKEL) (CHROMIUM - Manganese - Nickel) |
|||||||||||
| 304L(S30403) |
|
|
40 |
|
pa obligatwa | ||||||
A537Cl 1+304 L CLAD Aplikasyon Plak Steel
A537Cl 1+304 L plak asye yo te itilize nan konstriksyon nan pon, konstriksyon gran wout ak lòt konstriksyon jeni.
A537cl 1+304 l plak asye clad lòt non
A537cl 1+304 L plak asye clad, A537Cl1 plak asye, 304L plak asye
A537cl 1+304 l plak asye clad lòt non
UT (egzamen ultrasons), AR (tankou cho woule sèlman), TMCP (tèmik pwosesis kontwòl mekanik), N (normalized), Q+T (pasè ak apeze), z tès direksyon (Z15, Z25, Z35), Charpy V - tès enpak, tankou SG.
Adaptab a ba - tanperati presyon veso (egzanp, likid nitwojèn/tank depo oksijèn), kap founi bay A537Cl 1+304 L CLAD asye oswa P265GH +304 L CLAD asye konfòme a GB/T 3531. Low - Endikatè rezistans tanperati, oswa Customize konbinezon epesè espesyal, voye yon ankèt pou sipò teknik nan entegrasyon sistèm ba-tanperati.