ASTM A36 se asye ki pi souvan itilize grav ak cho woule. Li gen pwopriyete ekselan soude epi li apwopriye pou fanm k'ap pile, pwensonaj, frapan, perçage ak pwosesis machin. Fòs sede ASTM A36 se mwens pase woulo liv frèt C1018, kidonk pèmèt ASTM A36 pliye pi fasil pase C1018. Nòmalman, pi gwo dyamèt nan ASTM A36 yo pa pwodui depi C1018 woulo liv cho yo itilize.
ASTM A36 anjeneral disponib nan fòm sa yo:
Rektang ba
Bar kare
Baton sikilè
Fòm asye tankou chanèl, ang, H-travès ak I-travès.
Konpozisyon chimik
| Eleman | Kontni |
|---|---|
| Kabòn, C | 0.25 - 0.290 % |
| Kwiv, Cu | 0.20 % |
| Iron, Fe | 98.0 % |
| Manganèz, Mn | 1.03 % |
| Fosfò, P | 0.040 % |
| Silisyòm, Si | 0.280 % |
| Souf, S | 0.050 % |
Pwopriyete Fizik
| Pwopriyete Fizik | Metrik | Imperial |
|---|---|---|
| Dansite | 7.85 g/cm3 | 0.284 lb/pous3 |
Pwopriyete mekanik
| Pwopriyete mekanik | Metrik | Imperial |
|---|---|---|
| Fòs rupture, ultim | 400 - 550 MPa | 58000 - 79800 psi |
| Fòs rupture, Sede | 250 MPa | 36300 psi |
| Elongasyon nan kraze (nan 200 mm) | 20.0 % | 20.0 % |
| Elongasyon nan kraze (nan 50 mm) | 23.0 % | 23.0 % |
| Modil Elastisite | 200 GPa | 29000 ksi |
| Modil Bulk (tipik pou asye) | 140 GPa | 20300 ksi |
| Poissons rapò | 0.260 | 0.260 |
| Chea modil | 79.3 GPa | 11500 ksi |