R60702 se klase kòm Ameriken Creole Zirconium, zirkonyòm Tib Specification Pwogrè: ASTM B523/B523M-2012A, Zirconium baton Specification Specification: ASTM B550/B550M-2007, Zirconyòm Plak Specification Specification: ASTM B551/B551-201M-
R60702 Karakteristik zirkonyòm: zirkonyòm se yon metal ki ra, ak rezistans korozyon etonan, pwen trè wo fonn, dite super ak fòs ak lòt karakteristik, se lajman ki itilize nan avyon, militè, reyaksyon nikleyè, jaden enèji atomik.
R60702 Itilizasyon zirkonyòm: Zirconium se yon materyèl enpòtan nan envantè zam tankou tank, tank, kanon ak plak bal.
zirkonyòm R60702 konpozisyon chimik tiyo
Klas zirkonyòm
ZR 702
ZR 704
ZR705
Ògje
R60702
R60704
R60705
Zirkonyòm + hafnium (min)
99.2
97.5
95.5
Hafnium (max
4.5
4.5
4.5
Iron + CHROMIUM
0.2 max
0.2-0.4
0.2 max
Fèblan
-
1.0-2.0
-
Idwojèn (max)
0.005
0.005
0.005
Azòt (Max)
0.025
0.025
0.025
Kabòn (max)
0.05
0.05
0.05
Niobium
-
-
2.0-3.0
Oksijèn (max)
0.16
0.18
0.18
R60702 Zirconium Tib pwopriyete mekanik
Pwopriyete fizik
Metrik
Angle
Kòmantè
Densite
6.5 g/cc
0.235 lb/nan3
Pwopriyete mekanik
Dite, Rockwell A
49
49
Estime soti nan Vickers
Dite, Rockwell B
78
78
Estime soti nan Vickers
Dite, Vickers
150
150
Rkwir echantiyon
Fòs rupture, ultim
Min 379 MPa
Min 55000 psi
Fòs rupture, sede
Min 207 MPa
Min 30000 psi
0.2% ys
Elongasyon nan repo
16 %
16 %
Nan 50 mm
Modil Elastisite
99.3gpa
14400 ksi
Rapò Poisson an
0.35
0.35
Fòs fatig
125 MPa
18100 psi
5 e +5 sik, rache
Fòs fatig
145 MPa
21000 psi
3 e +7 sik, unnotched
Fòs fatig
175 MPa
25400 psi
5 e +3 sik, unnotched
Fòs fatig
60 MPa
8700 psi
3 e +7 sik, rache
Chea modil
36.2 GPA
5250 ksi
Pwopriyete elektrik
Rezistivite elektrik
3.97e - 005 ohm-cm
3.97e - 005 ohm-cm
Koyefisyan temp se 0.0044/ degre nan 20 degre
Mayetik emotivite
1.34E-06
1.34E-06
CGS/G; Zr pi
Kritik fòs mayetik jaden, oersted
47
47
Zr pi
Tanperati kritik superconducting
0.595 - 0.625 K
0.595 - 0.625 K
Zr pi
Pwopriyete tèmik
Chalè fizyon
250 J/g
108 BTU/LB
CTE, lineyè 20 degre
5.89 µm/m - degre
3.27 µin/nan - degre f
nan 25 degre
CTE, lineyè 250 degre
6.3 µm/m - degre
3.5 µin/nan - degre f
CTE, lineyè 500 degre
6.9 µm/m - degre
3.83 µin/nan - degre f
Kapasite chalè espesifik
0.285 J/G - degre
0.0681 Btu/lb - degre f
Konduktiviti tèmik
22 W/m-K
153 btu - nan/hr - ft2- degre f
Pwen k ap fonn
1852 degre
3370 degre f
Pwopriyete optik
Emisyon (0-1)
0.32
0.32
650 nm; unoxidized pi bon kalite ZR echantiyon; total