Konpozisyon chimik ( %):
|
Klas/ materyèl |
Eleman |
Konpozisyon (Max-A, Min-mwen) |
|
Din en 10028-5 p460ml2 |
C |
A:0.16 |
|
Mn |
A:1.70 |
|
|
Si |
A:0.60 |
|
|
P |
A:0.020 |
|
|
S |
A:0.015 |
Pwopriyete mekanik (MPa)
|
Klas/ materyèl |
Tès èkstansibl |
MPA |
|
Din en 10028-5 p460ml2 |
Fòs rupture |
530-720 |
|
Sede fòs |
I:460 |
|
|
Elongasyon |
I:17% |
|
|
Tès enpak (si genyen) |
-50 degre |
1. Kijan pwosesis TMCP a diferan pou pwodiksyon P460ML2?
Repons:
Karakteristik yo ki nan pwosesis tèmomekanik kontwole:
Pi wo fini tanperati woule(800-880 degre vs 750-850 degre)
Pi dousman pousantaj refwadisman(5-15 degre /s vs 10-30 degre /s)
Redwi microalloying(NB mwens pase oswa egal a 0.04% vs 0.05%)
Si ou vle tanperaman for thickness >60mm
Sa ki lakòz nan20% sik pwodiksyon pi vit
2. Ki paramèt soude yo rekòmande?
Repons:
Pwosedi soude ki kalifye:
Chèz: 150-200°C (for t>20mm)
Consommables: En iso 16834- Ag 55 5 M 21 3 Ni1mo
Chalè opinyon: 1.8-3.0 kj/mm
Entèrpass temp: 150-220 degre
PWHT: 600-620°C × 1hr/25mm (t>40mm)
Tès: Enpak nan-40 degre
Nòt kritik:
• Pase rasin mande pouTIG soude
• Kontwòl idwojèn (<5ml/100g deposit)
• Sondaj diteObligatwa (max 350hv10)
3. Kilè enjenyè yo ta dwe presize P460ML2?
Repons:
Ideyal pou:
✔ Depo frijidè(-40 degre)
✔ Veso Pwosesis Chimik
✔ Pwojè kriyojenik pri-sansib
✔ Epesè ranje 20-80 mm
Pa rekòmande pou:
✖ LNG Prensipal KONTINYE (-162 degre)
✖ SÈVIS SOUR (anviwònman H2S)
✖ Thick sections (>100mm) ki egzije pwopriyete z-direksyon
Baj popilè: en 10028-5 p460ml2 pou plak veso presyon, Lachin en 10028-5 p460ml2 pou manifaktirè plak veso presyon, founisè, faktori