GB/T 16270 Q620D plak asye ki ba alyaj gen bon fòs, plastisit ak severite, bon soudabilite ak pèfòmans pwosesis cho ak frèt peze, ak bon rezistans korozyon.
Q620D asye se sitou itilize nan envantè de aparèy mekanik ak lòt pati estriktirèl, tankou perçage forage, pèl elektrik, pouvwa-kondwi kamyon min kontwa wou, pwodwi mineral machin, pneu, chajè, elatriye.
Lachin GB/T16270 Q620D Low-alyaj segondè-fòs plak asye konpozisyon chimik ak pwopriyete mekanik:
| KLAS STEEL | C% 25 max | Si% max | Mn% max | P% max | S% 25 max | Cu% max | Cr% max | Ni% 25 max | Mo % max | B % max | V % max | Nb% max | Ti % max |
| Q620D | 0.2 | 0.80 | 1.7 | 0.02 | 0.010 | 0.5 | 1.5 | 2 | 0.70 | 0.005 | 0.12 | 0.06 | 0.05 |
| KLAS STEEL | Re sede fòs Mpa min | Re sede fòs Mpa min | elongasyon % | Enèji ak tanperati | |||||||
| Min | 0 | -20 | -40 | -60 | |||||||
| t Mwens pase oswa egal a 50 | 50-100 | 100-150 | t Mwens pase oswa egal a 50 | 50-100 | 100-150 | J | J | J | J | ||
| Q620D | 620 | 580 | 560 | 700-890 | 700-890 | 650-830 | 15 | 47 | 47 | 34 | 34 |