P420ML1 ak P420ML2 se tou de plak asye thermomechanically woule pou veso presyon ak chodyèr, dapre EN 10028 -5 estanda. Diferans kle a se rezistans enpak ba-tanperati yo: P420ML1 espesifye pou tès enpak nan-40 degre, pandan y ap P420ML2 espesifye pou tès enpak nan-50 degre. Tou de klas yo gen yon fòs sede minimòm de 420 MPa ak bon soudabilite.
Teknoloji Siplemantè: Tès HIC|NACE MR0175|Z15|Z25|Z35
Epesè: 6MM a 300MM,
Lajè: 1500mm a 4050mm,
Longè: 3000mm a 15000mm
|
P420ML2Konpozisyon chimik |
|||||||
|
Klas |
Eleman Max (%) |
||||||
|
C |
Si |
Mn |
P |
S |
Al |
N |
|
|
P420ML2 |
0,16 |
0,50 |
1,70 |
0,020 |
0,015 |
0,020 |
0,020 |
|
Nb |
V |
Ti |
Ni |
Mo |
|
|
|
|
0,05 |
0,10 |
0,05 |
0,50 |
0,20 |
|
|
|
Ekivalan kabòn: Ceq=【C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15】%
P420ML1 Konpozisyon chimik
|
Klas / Materyèl |
Eleman |
Konpozisyon( Max-A, Min-I) |
|
DIN EN 10028-5 P420ML1 |
C |
A:0.16 |
|
Mn |
A:1.70 |
|
|
Si |
A:0.50 |
|
|
P |
A:0.020 |
|
|
S |
A:0.015 |
|
Klas |
P420ML2 Pwopriyete mekanik |
|||
|
Epesè |
Sede |
Tensile |
Elongasyon |
|
|
P420ML2 |
mm |
Min Mpa |
Mpa |
% min |
|
6-16 |
420 |
500-660 |
19% |
|
|
16-40 |
400 |
500-660 |
19% |
|
|
40-63 |
390 |
500-660 |
19% |
|
P420ML1 Pwopriyete mekanik
|
Klas / Materyèl |
Tès Tensile |
MPa |
|
DIN EN 10028-5 P420ML1 |
Fòs rupture |
500-660 |
|
Sede fòs |
I:420 |
|
|
Elongasyon |
I:19% |
|
|
Tès enpak (si genyen) |
-40 degre |