Plak asye LR klas DH50 Shipbuilding se sitou itilize nan pwojè konstriksyon bato ak pwojè estriktirèl lanmè lanmè.
LR Grade DH50 Shipbuilding Steel Plate Lòt Non
LR Grade DH50 Shipbuilding asye plak, LR Klas DH50 Plak asye bato, LR Klas DH50 Plak asye Marin, LR Klas DH50 plak asye.
Kondisyon adisyonèl
UT (Egzamen Ultrasonic), AR (Kòm woule cho sèlman), TMCP (Tèmik Pwosesis kontwòl mekanik), N (Normalize), Q + T (Tenn ak Tanperaman), Tès Direksyon Z (Z15, Z25, Z35), Tès Enpak Charpy V - Notch, Tès Twazyèm Pati (tankou Tès SGS), kouvwi ak pating.
|
LR DH50 siplemantè segondè fòs chimik konpozisyon |
|||||||
|
Klas |
Eleman Max (%) |
||||||
|
C |
Si |
Mn |
P |
S |
Al |
N |
|
|
LR DH50 |
0.20 |
0.55 |
1.70 |
0.030 |
0.030 |
0.015 |
0.020 |
|
Nb |
V |
Ti |
Cu |
Kr |
Ni |
Mo |
|
|
0.02-0.05 |
0.03-0.10 |
0.02 |
|
|
|
|
|
Sansiblite krak: Pcm=(C+Si/30+Mn/20+Cu/20+Ni/60+Cr/20+Mo/15+V/10+5B)%
Ekivalan kabòn: Ceq=【C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15】%
|
LR DH50 pwopriyete siplemantè segondè fòs |
|||||||
|
Klas |
|
Pwopriyete mekanik |
Tès enpak Charpy V |
||||
|
Epesè |
Sede |
Tensile |
Elongasyon |
Degre |
Enèji 1 |
Enèji 2 |
|
|
LR DH50 |
mm |
Min Mpa |
Mpa |
% min |
-20 |
J |
J |
|
t Mwens pase oswa egal a 50 |
500 |
610-770 |
18% |
33 |
50 |
||
|
50＜t Mwens pase oswa egal a 70 |
500 |
610-770 |
18% |
33 |
50 |
||
|
70＜t Mwens pase oswa egal a 100 |
500 |
610-770 |
18% |
33 |
50 |
||
|
Remak: Enèji 1 se tès enpak transverse, Enèji 2 se longitudinal |
|||||||