S355J2W ak S355K2W se dezagreyab (W) asye estriktirèl anba estanda EN 10025-5 ak yon fòs sede minimòm de 355 MPa, diferan prensipalman nan kondisyon enèji enpak espesifik yo, ak 'K2' ki endike yon enèji tès enpak pi wo (anjeneral 40J) pase 'J27J' nan rezistans korozyon, epi ki fè yo apwopriye pou korozyon aplikasyon pou ba-tanperati, fòme yon kouch rouye pwoteksyon sou tan.
Konpozisyon chimik nan analiz pwodwi klas S355J2W
|
C |
Si |
Mn |
Cu |
P |
S |
Kr |
N |
|
0.19 |
0.55 |
0.45-1.60 |
0.20-0.60 |
0.035 |
0.035 |
0.35-0.85 |
0.010 |
Konpozisyon chimik nan analiz pwodwi klas S355K2W
|
C |
Si |
Mn |
Cu |
P |
S |
Kr |
N |
|
0.19 |
0.55 |
0.45-1.60 |
0.20-0.60 |
0.035 |
0.035 |
0.35-0.85 |
0.010 |
Pwopriyete mekanik nan klas S355J2W
|
Tanperati |
-20 |
-10 |
0 |
20 |
|
Tès enpak Notch. Min. enèji absòbe J |
27 |
|
Epesè nominal (mm) |
rive 16 |
16 - 40 |
40 - 63 |
63 - 80 |
80 - 100 |
100 - 150 |
|
ReH - Minimòm fòs sede (MPa) |
355 |
345 |
335 |
325 |
315 |
295 |
|
Epesè nominal (mm) |
rive 3 |
3 - 100 |
100-150 |
|
Rm -Fòs rupture (MPa) |
510-680 |
470-630 |
450-600 |
|
Epesè nominal (mm) |
Pi gran pase oswa egal a 1.5＜2 |
Pi gran pase oswa egal a 2﹤2.5 |
Pi gran pase oswa egal a 2.5＜3 |
Pi gran pase oswa egal a 3＜40 |
Pi gran pase oswa egal a 40﹤63 |
Pi gran pase oswa egal a 6﹤100 |
Pi gran pase oswa egal a 100﹤150 |
|
A - elongasyon minimòm Lo=5,65 √ So (%) Longitudinal |
16 |
17 |
18 |
22 |
21 |
20 |
18 |
Pwopriyete mekanik nan klas S355K2W
|
Tanperati |
-20 |
-10 |
0 |
20 |
|
Tès enpak Notch. Min. enèji absòbe J |
40 |
|
|
|
|
Epesè nominal (mm) |
rive 16 |
16 - 40 |
40 - 63 |
63 - 80 |
80 - 100 |
100 - 150 |
|
ReH - Minimòm fòs sede (MPa) |
355 |
345 |
335 |
325 |
315 |
295 |
|
Epesè nominal (mm) |
rive 3 |
3 - 100 |
100-150 |
|
Rm -Fòs rupture (MPa) |
510-680 |
470-630 |
450-600 |
|
Epesè nominal (mm) |
Pi gran pase oswa egal a 1.5＜2 |
Pi gran pase oswa egal a 2﹤2.5 |
Pi gran pase oswa egal a 2.5＜3 |
Pi gran pase oswa egal a 3＜40 |
Pi gran pase oswa egal a 40﹤63 |
Pi gran pase oswa egal a 6﹤100 |
Pi gran pase oswa egal a 100﹤150 |
|
A - elongasyon minimòm Lo=5,65 √ So (%) Longitudinal |
16 |
17 |
18 |
22 |
21 |
20 |
18 |
Diferans kle yo
W (Weathering): Tou de klas yo gen 'W' ki endike amelyore rezistans korozyon atmosferik akòz eleman alyaj te ajoute (tankou Cu, Cr, Ni, Mo) ki fòme yon kouch oksid ki estab, pwoteksyon, elimine bezwen pou penti nan anpil aplikasyon.
J2 kont K2 (Enèji enpak):
S355J2W: Egzije yon nivo enèji enpak espesifik (egzanp, 27 Joules nan yon sèten tanperati).
S355K2W: Egzije yon nivo enèji enpak ki pi wo (egzanp, 40 Joules nan menm tanperati a).
Creole: Yo tonbe anba EN 10025 -5:2004, ki kouvri cho-woule asye estriktirèl ak amelyore rezistans korozyon atmosferik.