ASTM A588Grade C(A588GRC)) Plak asye yo itilize nan konstriksyon pon, konstriksyon gran wout ak lòt konstriksyon jeni.
Lòt Non
ASTM A588Grade C(A588GRC)) Kabòn Plak Steel,|ASTM A588Grade C(A588GRC)) Plak ki gen gwo fòs,|ASTM A588Grade C(A588GRC)) Plak Kabòn,|ASTM A588Grade C(A588GRC)) Plak.
Kondisyon adisyonèl
UT (Egzamen Ultrasonic), AR (Kòm woule cho sèlman), TMCP (Tèmik Pwosesis kontwòl mekanik), N (Normalize), Q + T (Tenn ak Tanperaman), Tès Direksyon Z (Z15, Z25, Z35), Tès Enpak Charpy V - Notch, Tès Twazyèm Pati (tankou Tès SGS), kouvwi ak pating.
Chemical Composition of A588 Grade C
|
ASTM A588 konpozisyon chimik |
|||||||
|
Klas |
Eleman Max (%) |
||||||
|
C |
Si |
Mn |
P |
S |
Ni |
Nb |
|
|
A588 |
0.15 |
0.15-0.40 |
0.80-1.35 |
0.04 |
0.05 |
0.20-0.50 |
.. |
|
Cu |
Kr |
Mo |
N |
V |
|
|
|
|
0.20-0.50 |
0.30-0.50 |
… |
0.010 |
0.02-0.10 |
|
|
|
Ekivalan kabòn: Ceq=【C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15】%
Pwopriyete mekanik A588 Klas C
|
Pwopriyete mekanik nan plak asye A588 Klas C |
A588 Klas C |
|
Fòs rupture, bo [MPa] |
Fòs rupture, bo [MPa] |
|
100mm oswa anba |
[485] |
|
100mm-125mm |
[460] |
|
125mm-200mm |
[435] |
|
Sede fòs, min, kis [MPa] |
Sede fòs, min, kis [MPa] |
|
100mm oswa anba |
[345] |
|
100mm-125mm |
[315] |
|
125mm-200mm |
[290] |
|
Elongasyon nan anba. [50 mm], min, % |
21 |
|
Elongasyon nan anba. [50 mm-200mm], min, % |
18 |