Diferan prensipal la se nan konpozisyon chimik ASTM A514GRA ak konpozisyon chimik A514GRB. Materyèl asye A514GRA te ajoute eleman zirkonyòm, ak materyèl asye A514GRB te ajoute eleman Vanadyòm ak Titàn lè woule.
Tou de se gwo -fòs, trempe ak apeze plak asye alyaj ak pwopriyete mekanik menm jan an, ki gen ladan yon fòs sede minimòm de 100,000 psi (690 MPa) ak yon fòs rupture nan 110,000-130,000 psi (760-895 MPa).
|
Segondè fòs steel klas yo A514GrAvsA514GrB |
Konpozisyon chimik: analiz chalè Max% |
|||||||||||
|
Estanda |
Klas |
C |
Mn |
P |
S |
Si |
Kr |
Mo |
V |
Ti |
Zr |
B |
|
ASTM A514/A514M |
A514GrA |
0.15-0.21 |
0.8-1.1 |
0.035 |
0.035 |
0.4-0.8 |
0.5-0.8 |
0.18-0.28 |
/ |
/ |
0.15-0.5 |
0.0025 |
|
ASTM A514/A514M |
A514GrB |
0.12-0.21 |
0.7-1.0 |
0.035 |
0.035 |
0.2-0.35 |
0.4-0.65 |
0.15-0.25 |
0.03-0.08 |
0.01-0.03 |
/ |
0.0005- 0.005 |
|
Pwopriyete mekanik: |
Epesè |
Sede fòs |
Fòs rupture |
|||||||||
|
Mpa Min. |
Mpa |
|||||||||||
|
ASTM A514/A514M |
A514GrA |
T Mwens pase oswa egal a 65 |
690 |
760-895 |
||||||||
|
ASTM A514/A514M |
A514GrB |
T Mwens pase oswa egal a 65 |
690 |
760-895 |
||||||||