Q345r +304 CLAD asye plak konpozisyon chimik ak pwopriyete mekanik
|
Egalize |
C % |
Si % |
Mn % |
Cu % |
Ni % |
Cr% |
Mo % |
V % |
|
Q345R |
0.20 |
0.55 |
1.2-1.7 |
0.30 |
0.30 |
0.30 |
0.08 |
0.050 |
|
Ti % |
Alt % |
P % |
S % |
NB |
|
|
|
|
|
0.030 |
0.020 |
0.025 |
0.010 |
0.050 |
|
|
|
|
Egalize |
Epesè (mm) |
Min sede |
Raman |
Elongasyon |
Min enèji enpak |
|
|
|
|
|
|
|
Degre |
Min j |
|
Q345R |
3-16 |
345MPA |
510-640 MPa |
21% |
0 |
41J |
|
16-36 |
325MPA |
500-630 MPa |
21% |
0 |
41J |
|
|
36-60 |
315 MPa |
490-620 MPa |
21% |
0 |
41J |
|
|
60-100 |
305 MPa |
490-620 MPa |
20% |
0 |
41J |
|
|
100-150 |
285 MPa |
480-610 MPa |
20% |
0 |
41J |
|
|
150-250 |
265 MPa |
470-600 MPa |
20% |
0 |
41J |
|
| Egalize |
C
|
Mn |
P
|
S
|
Si |
Cr |
NI | Mwa | NI |
Koper
|
| 304(S30400) | 0.07 | 2.0 | 0.045 | 0.030 | 0.75 | 17.5-19.5 | 8.0-10.5 | - | 0.10 | - |
| Egalize |
Sede fòs (N/mm2), min |
Fòs rupture (N/mm2), min |
Elongationin 2 pous (50mm), %, min |
|
Fwad Bend | ||||||
|
Austenitic (CHROMIUM - Nikèl) (CHROMIUM - Manganese - Nickel) |
|||||||||||
| 304(S30400) |
|
|
40 |
|
pa obligatwa | ||||||
Q345R +304 aplikasyon plak asye rekouvèr
Q345R +304 plak asye rekouvèr yo te itilize nan konstriksyon nan pon, konstriksyon gran wout ak lòt konstriksyon jeni.
Q345r +304 Plak asye rekouvèr Lòt Non
Q345r +304 plak asye rekouvèr, Q345R plak asye, 304 plak asye
Lòt kondisyon
UT (egzamen ultrasons), AR (tankou cho woule sèlman), TMCP (tèmik pwosesis kontwòl mekanik), N (normalized), Q+T (pasè ak apeze), z tès direksyon (Z15, Z25, Z35), Charpy V - tès enpak, tankou SG.
Aplikab a LNG depo/sistèm transpò nan sektè enèji a, adopte plak asye rekouvèr tankou P265GH +410 CLAD asye (pou ba - tanperati severite) oswa Q345R +304 CLAD asye. Si ou vle verifye -162 pèfòmans enpak degre, konpatibilite izolasyon vakyòm, oswa Customize espesifikasyon pou tank LNG gwo, kontakte nou jwenn paramèt teknik ak quotes rapid.